VICTREX 450G™ MIC PEEK POLYMER |
| High performance thermoplastic material, unfilled PolyEtherEtherKetone (PEEK), semi crystalline, micropellets for compression moulding, standard flow, colour natural. |
| Material Properties | |||
| Physical | Nominal Value | Unit | Test Method |
| Density 1 | 1.30 | g/cm³ | ISO 1183 |
| Apparent (Bulk) Density | 0.75 | g/cm³ | ISO 1183 |
| Average Particle Size D50 | 1.5 x 1.8 mm | | ISO 13320-1 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 1 (23°C) | 4000 | MPa | ISO 527-1 |
| Tensile Stress | |||
| Yield, 23°C 1 | 98.0 | MPa | ISO 527-2 |
| Break, 23°C | 82.0 | MPa | ISO 527 |
| Tensile Strain (Break, 23°C) | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% Strain, 23°C | 122 | MPa | |
| 5.0% Strain, 23°C | 151 | MPa | |
| 23°C 2 | 164 | MPa | |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/A |
| Hardness | Nominal Value | Unit | Test Method |
| Shore Hardness 1 (Shore D, 23°C) | 84.5 | | ISO 868 |
| Thermal | Nominal Value | Unit | Test Method |
| Glass Transition Temperature 1 | ISO 11357-2 | ||
| Onset | 143 | °C | |
| Midpoint | 150 | °C | |
| Melting Temperature 1 | 343 | °C | ISO 11357-3 |
| Fill Analysis | Nominal Value | Unit | Test Method |
| Melt Viscosity 1 (400°C) | 350 | Pa·s | ISO 11443 |
| Additional Information | Nominal Value | Unit | Test Method |
| Compression Molding Temperature | 380 to 400 | °C | |
| Drying Temperature Compression molding | 120 to 150 | °C | |
| Drying Time Compression molding | 3.0 to 5.0 | hr | |
| Important notes: | |||
| Notes |
| 1Data inherited from 450G. |
| 2Maximum strain |