Go back to datasheets

VICTREX™ PEEK POLYMER 650PF

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression moulding, low flow, colour natural.

Material Properties
Physical

Nominal Value

Unit

Test Method

Density

1.30

g/cm³

ISO 1183

Apparent (Bulk) Density

0.30

g/cm³

ISO 1183

Average Particle Size - D50

75

µm

ISO 13320-1
Mechanical

Nominal Value

Unit

Test Method

Tensile Modulus (23°C)

3900

MPa

ISO 527-1

Tensile Stress (Yield, 23°C)

90.0

MPa

ISO 527-2

Tensile Strain (Break, 23°C)

30

%

ISO 527-2

Flexural Modulus (23°C)

3600

MPa

ISO 178

Flexural Stress (23°C)

150

MPa

ISO 178
Impact

Nominal Value

Unit

Test Method

Notched Izod Impact Strength (23°C)

7.5

kJ/m²

ISO 180/A

Unnotched Izod Impact Strength (23°C)

No Break

ISO 180
Thermal

Nominal Value

Unit

Test Method

Glass Transition Temperature

ISO 11357-2

Onset

143

°C

Midpoint

150

°C

Melting Temperature

343

°C

ISO 11357-3
Fill Analysis

Nominal Value

Unit

Test Method

Melt Viscosity (400°C)

500

Pa·s

ISO 11443
Additional Information

Nominal Value

Unit

Test Method

Compression Molding Temperature

380 to 400

°C

Drying Temperature - Compression molding

120 to 150

°C

Drying Time - Compression molding

3.0 to 5.0

hr

Typical Processing Information
Injection Notes

Important notes:

1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories

  • Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions.
  • Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould.
  • Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions.

2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions.

Detailed data available on our website www.victrex.com or upon request.