VICTREX PEEK 90G - Datasheet (JA)

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for injection moulding, very easy flow, colour natural/beige.

Complex geometries with thinner cross sections or longer flow lengths, for high strength and stiffness as well as good ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications

Material Properties
Physical	Nominal Value	Unit	Test Method
Density (Crystalline)	1.30	g/cm³	ISO 1183
Spiral Flow			Internal Method
--¹	24.5	cm
--²	28.0	cm
--³	33.0	cm
Molding Shrinkage⁴			ISO 294-4
Across Flow	1.3	%
Flow	1.0	%
Water Absorption (Saturation, 23°C)	0.45	%	ISO 62
Water Absorption Saturation (100°C)	0.55	%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	4100	MPa	ISO 527-1
Tensile Stress (Yield, 23°C)	105	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	15	%	ISO 527-2
Flexural Modulus (23°C)	3900	MPa	ISO 178
Flexural Stress			ISO 178
3.5% Strain, 23°C	130	MPa
23°C⁵	175	MPa
125°C	90.0	MPa
175°C	20.0	MPa
275°C	13.5	MPa
Compressive Stress			ISO 604
23°C	130	MPa
120°C	80.0	MPa
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179
Notched Izod Impact Strength (23°C)	4.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	No Break		ISO 180
Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 23°C)	85.0		ISO 868
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ISO 75-2/Af
1.8 MPa, Unannealed	156	°C
1.8 MPa, Annealed⁶	167	°C
Glass Transition Temperature (Onset)	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
CLTE - Flow			ISO 11359-2
< 143°C	50	ppm/K
> 143°C	120	ppm/K
CLTE - Average			ISO 11359-2
< 143°C	55	ppm/K
> 143°C	140	ppm/K
Thermal Conductivity			ISO 22007-4
23°C⁷	0.29	W/m/K
23°C⁸	0.32	W/m/K
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity			IEC 60093
23°C	1.0E+16	ohms·cm
125°C	1.0E+15	ohms·cm
275°C	1.0E+9	ohms·cm
Dielectric Strength (2.00 mm)	23.0	kV/mm	IEC 60243-1
Dielectric Constant (23°C, 1 kHz)	3.10		IEC 60250
Dissipation Factor (23°C, 1 MHz)	4.0E-3		IEC 60250
Comparative Tracking Index	150	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (2.0 mm)	960	°C	IEC 60695-2-12
Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	90.0	Pa·s	ISO 11443

Typical Processing Information
Injection	Nominal Value	Unit
Drying Temperature	120 to 150	°C
Drying Time	3.0 to 5.0	hr
Suggested Max Moisture	0.020	%
Hopper Temperature	< 100	°C
Rear Temperature	350	°C
Middle Temperature	355	°C
Front Temperature	355	°C
Nozzle Temperature	360	°C
Mould Temperature	160 to 200	°C
Injection Notes
Drying Temperature / Time: 150°C / 3h or 120°C / 5h (residual moisture <0.02%) Runner: Die / nozzle >3mm, manifold >3.5mm Gate: >1mm or 0.5 x part thickness Important notes: 1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions. Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould. Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions. 2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions. Detailed data available on our website www.victrex.com or upon request.

Notes

¹Mould Temperature: 160°C, Melt Temperature: 365°C, 1.00 mm

²Mould Temperature: 180°C, Melt Temperature: 375°C, 1.00 mm

³Mould Temperature: 200°C, Melt Temperature: 400°C, 1.00 mm

⁴360°C nozzle, 160°C tool

⁵At yield

⁶200°C/4h

⁷Average

⁸Along flow